Puncture resistant heat shrinkable film containing narrow molecular weight ethylene alpha olefin

ABSTRACT

A biaxially stretched film with very high heat shrink and puncture resistance properties, formed of low density ethylene alpha olefin copolymer having low melt index, low Mw/Mn, low melting point and low Young&#39;s Modulus.

FIELD OF THE INVENTION

This invention relates to puncture resistant, heat shrinkable film, and more particularly to such films having high puncture resistance, high biaxial heat shrink and good optical properties. The film contains ethylene alpha olefin copolymer with high molecular weight but a relatively narrow distribution of molecular weights (low Mw/Mn).

BACKGROUND OF THE INVENTION

The shrink packaging of food articles such as poultry, fresh red meat and processed meat products requires tough, puncture resistant, yet flexible film materials which are heat shrinkable. Most commonly these films are fabricated as bags into which the food articles are placed. The food article-containing bag is then evacuated and sealed either by clips or more commonly by heat sealing the bag inner surfaces together across the bag's open mouth end. The sealed, food article-containing bag is then heated, for example by hot air, infrared radiation or hot water, causing the bag to shrink in both the machine direction (MD) and the periodically inspected to insure continued package integrity.

For example, in commercial poultry shrink packaging operations, monolayer films formed from polyethylene or ethylene vinyl acetate polymers have been widely used. In general, polyethylenes such as linear low density polyethylene (LLDPE) and high density polyethylene (HDPE) provide relatively high puncture resistance, high tensile strength, but relatively low biaxial shrink properties. On the other hand, ethylene vinyl acetate (EVA) provides relatively high shrink and limited tensile strength/puncture resistance. In some instances blends of various polyethylenes and EVA have been used to obtain a balance of these desirable properties, but with limited success.

Monolayer films are suitable for poultry packaging. However for fresh red meat and processed meat packaging, a high degree of oxygen and moisture barrier protection is essential, so the common practice has been to use multilayer films including an oxygen barrier as a core layer between at least one inner layer and one outer layer. Oxygen barriers include vinylidene chloride copolymers such as the vinyl chloride form (saran) and the methyl acrylate form (MA saran), hydrolyzed ethylene vinyl acetate (EVOH) and nylon. The innermost layer of such multilayer films is in direct contact with the stored food and is frequently referred to as the sealing layer. This is because the most common method of sealing heat shrinkable food packages of this type is by heating the mouth edges of the self adhering inner layers together under pressure. That is, the opposite inner surfaces of the film enclosure are sealed by heat. So the inner layer must be formed of a self-adhering material which seals (but does not melt) over an elevated temperature range imparted by commercially used equipment such as impulse sealers. The most commonly used material for the inner layer is EVA, either alone or in a blend with other thermoplastic polymers such as polyethylenes. Typically this inner layer is also the thickest layer of the multilayer film. For example, in a 2.5 mil thick film the inner layer of a three layer film may comprise about 60% of this total thickness.

The outer layer of oxygen-barrier type multilayer films is often referred to as the abuse layer, because it must withstand abrasion from sliding contact with external objects during normal handling, as well as resistance to puncture from contact with external sharp articles. Outer layers are commonly formed of polyethylenes or EVA or blends thereof. Typically the outer layer of a three layer film comprise about 20-35%, the barrier layer comprises about 10-25%, and the inner layer comprises about 55-70% of the total film thickness.

It should also be recognized that since food articles such as primal and sub-primal fresh meat cuts often have sharp edges or protruding bones, the multilayer film must have good resistance to puncturing from the inside.

It has previously been indicated that whereas EVA affords high biaxial heat shrink properties, its strength properties such as tensile strength and puncture resistance are inferior to polyethylenes such as LLDPE, which unfortunately have relatively low biaxial heat shrink. These limitations have been partially overcome by the discovery of ethylene alpha olefin copolymers known as very low density polyethylene (hereinafter VLDPE), also called "ultra low density polyethylene" (ULDPE) and use of same in heat shrinkable films as for example described in Lustig et al U.S. Pat. No. 4,863,769. According to the latter, VLDPE may be used in either the aforedescribed monolayer films for non-barrier poultry shrink packaging or in the inner and/or outer layers of a multilayer oxygen barrier type film. When used in either manner, it provides substantially higher shrink than other polyethylenes such as LLDPE, yet imparts higher strength and puncture resistance than EVA. Accordingly, use of prior art types of VLDPE has permitted the practitioner to achieve biaxial heat shrink properties approaching those of EVA without sacrificing the high tensile strength/puncture resistance properties of polyethylene.

In addition to the prior art types of VLDPE, other ethylene alpha olefins are manufactured with elastomeric properties and these commercially available materials are hereinafter referred to as "prior art ethylene alpha olefin plastomers". Some of these have densities in the same range as VLDPE's but have greatly different physical properties due to differences in manufacturing processes. For example, it appears that prior art ethylene alpha olefin plastomers and VLDPE are manufactured with different catalyst systems. One manufacturer of these prior art materials is Mitsui Petrochemicals Ltd., and they sell prior art ethylenebutene plastomer copolymers under the name "Tafmer". These materials are used in blends with other thermoplastic polymers in various applications such as films to provide improved shrink, flexibility, and in some instances improved strength. However, unlike VLDPE's, these prior art ethylene alpha olefins are too weak for use as monolayer biaxially oriented heat shrinkable films in the pure component form. By way of illustration, the prior art Tafmer materials either cannot be extruded into a primary tube, or if this is accomplished cannot be expanded for biaxial orientation by the well-known double bubble method without bubble breakage.

While the prior art has improved the heat shrink and physical strength properties of biaxially stretched films (both monolayer and multilayer types) by using blends of thermoplastic polymers such as EVA, prior art VLDPE and prior art ethylene alpha olefin plastomers, there is a need for biaxially stretched films with even higher heat shrink and higher physical strength properties than heretofore available. Moreover in some instances such blending improves physical properties but adversely affects optical properties because of incompatibilities between blended resins.

One object of this invention is to provide a heat shrinkable biaxially stretched thermoplastic film with higher shrink properties than obtainable with EVA.

Another object is to provide a heat shrinkable biaxially stretched thermoplastic film with higher tensile strength properties than obtainable with prior art polyethylenes.

A further object is to provide a heat shrinkable biaxially stretched thermoplastic film with higher dynamic puncture resistance properties than obtainable with prior art polyethylenes.

A still further object is to provide a heat shrinkable biaxially stretched thermoplastic monolayer film formed of a single ethylene alpha olefin copolymer, with higher heat shrink, tensile strength and dynamic puncture resistance properties than obtainable with prior art EVA or polyethylenes.

Still another object is to provide a heat shrinkable biaxially stretched thermoplastic multilayer film of the oxygen barrier core layer type, with at least one inner or outer layer formed of an EVA-ethylene alpha olefin copolymer blend, with higher shrink, tensile strength and dynamic puncture resistance properties than obtainable with prior art EVA-polyethylene blends, yet good optical properties.

Other objects and advantages of this invention will be apparent from the ensuing disclosure and appended claims.

SUMMARY OF THE INVENTION

In accordance with the present invention there is provided a heat shrinkable, puncture resistant, biaxially stretched thermoplastic film suitable for use in fabricating bags for packaging food articles. This film comprises a polyethylene which is a linear copolymer of ethylene and higher alpha olefin containing from 4 to 8 carbon atoms, having a density between about 0.88 and about 0.905 g/cm³, a melt index not exceeding about 1.0 g/10 min, a molecular weight size distribution ratio Mw/Mn below about 3, a melting point below about 100° C., a Young's Modulus of below about 750 kg/cm², and wherein the film shrinks at least about 50 percent at a temperature of about 90° C. in at least one of the machine and transverse directions. As used herein, the ethylene alpha olefins copolymers includes terpolymers of ethylene and two higher alpha olefins containing 4 to 8 carbon atoms.

This film may be a monolayer wherein the above-described ethylene alpha olefin copolymer comprises the entire composition, or it may be blended with other thermoplastic polymers. The film may also be part of a multilayer construction such as the previously described oxygen barrier core layer type, wherein the above-described ethylene alpha olefin copolymer comprises at least a portion of at least one layer on one side of the core layer.

As will be explained hereinafter in more detail and substantiated by the working examples, this film accomplishes all of the aforedescribed objects, and in fact provides additional advantages over prior art films commercially used for shrink packaging food.

DETAILED DESCRIPTION OF THE INVENTION

The ethylene alpha olefin resins used to manufacture the films of this invention may be prepared by using the traditional Ziegler-Natta heterogeneous catalyst system as for example broadly described in the aforementioned Lustig et al U.S. Pat. No. 4,863,769. It is believed that one resin which is useful in this invention, Mitsui's Tafmer A-0585, was prepared by such a catalyst system. Alternatively, the same general type of ethylene alpha olefin resins may be prepared by a homogenous metallocene single-site catalyst system which in general produces molecular chains of more uniform length with more evenly spaced comonomer. Another result is narrower molecular weight distribution and composition. If necessary, according to the resin manufacturers a multistep polymerization process with a succession of different metallocene single-site catalysts is capable of producing virtually any desired final molecular weight distribution. This general type of system is described in Welborn U.S. Pat. No. 5,183,867 (assigned to Exxon) and European Patent application publication 0 416 815 A2 to G. F. Schmidt (assigned to Dow Chemical Company) both incorporated herein by reference, to the extent pertinent.

Although the ethylene alpha olefin copolymers useful in the practice of this invention are different from previously known VLDPE copolymers, they have at least some of the VLDPE properties as broadly described in the previously referenced Lustig et al U.S. Pat. No. 4,863,769 (hereinafter "Lustig et al '769"). Whereas according to Lustig et al '769 the VLDPE may have a density up to about 0.914, the ethylene alpha olefins of this invention have densities up to about 0.905 g/cm³. Likewise, according to Lustig et al '769, VLDPE materials may have densities as low as about 0.86 g/cm³, whereas ethylene alpha olefins of this invention have densities as low as about 0.88 g/cm³. Like previously known VLDPE materials, the ethylene alpha olefins useful in this invention may be extruded into monolayer heat shrinkable biaxially oriented films having high strength and high heat shrink. According to Lustig et al '769, this VLDPE shrink is at least about 30% at 90° C. in at least either the transverse or the machine direction. The films of this invention shrink at least about 50% in at least one of the machine and transverse directions at 90° C. Moreover as will be demonstrated, films of this invention also provide higher puncture strength than films prepared from previously known VLDPE materials.

As previously explained, films formed from the ethylene alpha olefin copolymers according to this invention have certain properties which are quite different from and nonanalogous to films containing prior art ethylene alpha olefin plastomers even though one manufacturer of both type resins, Mitsui, describes them in terms of the same tradename--Tafmer. Table A is a listing of representative prior art ethylene alpha olefin plastomers and their physical properties in the resin form.

Ethylene alpha olefin copolymers suitable for use in this invention are relatively high molecular weight, as reflected in the requirement that their melt index not exceed about 1.0 g/10 min, as measured by ASTM D-1238, condition E. In a preferred embodiment they have a weight average molecular weight Mw of at least about 180,000 g/mole. In another preferred embodiment they have a number average molecular weight Mn of at least about 83,000 g/mole.

                  TABLE A                                                          ______________________________________                                         Prior Art Ethylene Alpha-Olefin Plastomer                                      Physical Properties                                                            Type  Manufacturer                                                                               Property     Units   Value                                   ______________________________________                                         A-4085                                                                               Mitsui      Melt Index   g/10 min                                                                               3.6                                                       (D-1238)     (190° C.)                                                  Density      g/cc    0.88                                                      (D-1505)                                                                       Vicat Soften Pt.                                                                            °C.                                                                             54                                                        (D-1525)                                                                       Tensile Strength                                                                            kg/cm.sup.2                                                                            270                                                       At Break                                                                       (515 K 6301)*                                                                  Elongation   %       800                                                       At Break                                                                       (515 K 6301)*                                                                  Mw           g/mole  108,000                                                   Mn           g/mole  46,000                                                    Mw/Mn        none    2.35                                    A-4090                                                                               Mitsui      Melt Index   g/10 min                                                                               3.6                                                       (D-1238)     (190° C.)                                                  Density      g/cc    0.89                                                      (D-1505)                                                                       Vicat Soften Pt.                                                                            °C.                                                                             60                                                        (D-1525)                                                                       Tensile Strength                                                                            kg/cm.sup.2                                                                            320                                                       At Break                                                                       (515 K 6301)*                                                                  Elongation   %       700                                                       At Break                                                                       (515 L 6301)*                                                                  Mw/Mn        none    2.0                                     A-1085                                                                               Mitsui      Melt Index   g/10 min                                                                               1.4                                                       (D-1238)     (190° C.)                                                  Density      g/cc    0.885                                                     (D-1505)                                                                       Vicat Soften Pt.                                                                            ° C.                                                                            58                                                        (D-1525)                                                                       Tensile Strength                                                                            kg/cm.sup.2                                                                            340                                                       At Break                                                                       (515 K 6301)*                                                                  Elongation   %       710                                                       At Break                                                                       (515 K 6301)*                                                                  Mw           g/mole  160,000                                                   Mn           g/mole  80,000                                                    Mw/Mn        none    2.0                                     ______________________________________                                          *A Japanese test procedure similar to ASTM D638                          

Prior art VLDPE materials include those manufactured by Dow Chemical Company and Union Carbide Corporation, and Table B is a representative list along with physical properties in the resin form.

                  TABLE B                                                          ______________________________________                                         Prior Art VLDPE Physical Properties                                                    Manu-                                                                  Type    facturer  Property     Units  Value                                    ______________________________________                                         4001    Dow       Melt Index   g/10 min                                                                              1.0                                      also    (ethylene-                                                                               D-1238                                                       XU61520.01                                                                             octene-1  Density      g/cc   0.912                                            copolymer)                                                                               D-792                                                                          Tensile Yield                                                                               psi    1200                                                       D-638                                                                          Ultimate     psi    3500                                                       Tensile                                                                        D-638                                                                          Ult.Elongation                                                                              %      850                                                        D-638                                                                          Vicat Soften °C.                                                                            95                                                         Pt.                                                                            D-1525                                                                         Mw/Mn        none   5.1                                                        ASTM D-3593  (110,600/                                                                      21,680)                                         4003    Dow       Melt Index   g/10 min                                                                              0.8                                              (ethylene-                                                                               D-1238                                                               octene-1  Density      g/cc   0.905                                            copolymer)                                                                               D-792                                                                          Tensile Yield                                                                               psi    950                                                        D-638                                                                          Ultimate     psi    3200                                                       Tensile                                                                        D-638                                                                          Ult.Elongation                                                                              %      800                                                        D-638                                                                          Vicat        °C.                                                                            80                                                         Soften.Pt.                                                                     D-1525                                                       1137    Union     Melt Index   g/10 min                                                                              1.0                                              Carbide   D-1238                                                               (ethylene-                                                                               Density      g/cc   0.905                                            butene    D-792                                                                copolymer)                                                                               Tensile Yield                                                                               psi    2800                                                       D-638                                                                          Ultimate Tensile                                                                            psi    --                                                         D-638                                                                          Ult.Elongation                                                                              %      1720                                                       D-638                                                                          Vicat Soften Pt.                                                                            °C.                                                                            80                                                         D-1525                                                                         Mw/Mn        none   4.9                                                        ASTM D-3593         125,000/                                                                       25,700                                   1192    Union     Melt Index   g/10 min                                                                              0.19                                             Carbide   D-1238                                                               (ethylene-                                                                               Density      g/cc   0.912                                            butene-   D-792                                                                hexene    Tensile Strength                                                                            psi    7100 MD                                          ter-      D-882               5000 TD                                          polymer)  Ult.Elongation                                                                              %      400 MD                                                     D-882               760 TD                                                     Vicat Soften.Pt.                                                                            °C.                                                                            low 80's                                                   D-1525              reported                                                                       by mfg.                                                    Mw/Mn        none   12.2                                                       ASTM D-3593         196,900/                                                                       16,080                                   ______________________________________                                    

Suitable ethylene alpha olefins for preparing the film of this invention include Mitsui's Tafmer A-0585. Physical properties of Tafmer A-0585, an ethylenebutene copolymer, are set forth in Table C.

                  TABLE C                                                          ______________________________________                                         Tafmer A-0585 Physical Properties                                              Property         Unit        Value                                             ______________________________________                                         Melt Index       g/10 min    0.5                                               (D-1238)         (190° C.)                                              Density          g/cc        0.88                                              (D-1505)                                                                       Melting Point    °C.  67                                                Vicat Soften Pt. °C.  62                                                (D-1525)                                                                       Tensile Strength kg/cm.sup.2 400                                               At Break                                                                       (515 K 6301)                                                                   Elongation At    %           650                                               Break (515K                                                                    6301)                                                                          Mw               g/mole      190,000                                           Mn               g/mole      92,600                                            Mw/Mn            none        about 2                                           ______________________________________                                    

Molecular Weight/Size Distribution

Most commercial polymeric materials are polydisperse. This means they have a distribution of molecules with varying chain length, which distribution may be characterized by numerical averages.

Ethylene alpha-olefin copolymers may be partially characterized by their weight average molecular weight (Mw) which is determined by multiplying the weight of each chain length of a given number of repeat units by the number of such chain lengths present, and dividing by the total weight of chains. Mw is more sensitive to the longer chain length, i.e., larger molecules. Ethylene alpha-olefin copolymers may also be partially characterized by a number average molecular weight (Mn), which is derived from the total number of polymer molecules of each chain length present divided by the total number of chains present. Mn is particularly sensitive to shorter chain lengths, i.e., smaller molecules. When both Mw and Mn are known, they can be used to characterize the shape of the molecular weight distribution curve for the copolymer, i.e. the number of polymer chains in a molecular weight interval as the ordinate and the molecular weight as the abscissa. Qualitatively, a high Mw/Mn connotes a wide distribution of molecular weights whereas a low Mw/Mn connotes narrow distribution. Mw/Mn can be measured by several different techniques, but as used herein the gel permeation chromatography ("GPC") procedure outlined in ASTM D-3593- 80 is used.

In general, relatively narrow Mw/Mn distribution (and low ratio) permits sharper control of physical properties and superior optical properties, i.e. relatively high gloss and low haze. However, relatively low Mw/Mn ratio value prior art polymers are also difficult to process. More particularly, the specific prior art ethylene alpha-olefin plastomers known to applicant are characterized by relatively narrow molecular weight distribution and Mw/Mn values below about 3. They are relatively difficult to process into films by melt extrusion. Applicant has been unable to prepare biaxially oriented heat-shrinkable film from these materials such as the aforedescribed Tafmer A-1085 and Tafmer A-4085.

In contrast, although the ethylene alpha olefins useful in the practice of this invention have relatively low Mw/Mn values below 3, yet they can be used to form pure component biaxially stretched, heat shrinkable film. One probable reason is that although they have relatively narrow molecular weight distributions, their Mw and Mn values are substantially higher than the prior art ethylene alpha olefin plastomers. That is, their weight average molecular weight Mw is preferably at least about 180,000 g/mole and their number average molecular weight Mn is preferably at least about 83,000 g/mole.

In general, previously known VLDPE copolymers available in commercial quantities have substantially wider molecular weight distribution and higher Mw/Mn values (i.e. above about 3) than the prior art ethylene alpha olefin plastomers. As such, the previously known VLDPE copolymers have had higher impact strength, tensile strength, abrasion resistance and better processing characteristics. For example, by themselves these VLDPEs may be melt extruded into a primary tube and oriented into a heat shrinkable tube. The molecular weight/size distribution absolute values and Mw/Mn ratios for representative commercially available ethylene alphaolefin copolymers are set forth in the following Table D. Unless indicated otherwise, these values were measured by the GPC procedure of ASTM D-3593-80.

                  TABLE D                                                          ______________________________________                                         Molecular Weight/Size Distribution                                             Type Compound and Manufacturer                                                                     Mw/Mn**                                                    ______________________________________                                         Union Carbide 1085 VLDPE                                                                           3.6 (118,000/33,000)                                       (0.885 density, 0.8 MI)                                                        Union Carbide 1137 VLDPE                                                                           4.9 (125,000/25,700)                                       (0.900 density, 1.0 MI)                                                        Union Carbide 1192 VLDPE                                                                           12.2 (196,900/16,080)                                      (0.912 density, 0.19 MI)                                                       Union Carbide 1096-2 VLDPE                                                                         7.2 (137,000/19,110)                                       (0.912 density, 0.38 MI)                                                       Dow 4001 VLDPE      5.1 (110,600/21,680)                                       (0.912 density, 1.0 MI)                                                        Mitsui 0.896 density VLDPE                                                                         4.0*                                                       Mitsui 0.907 density VLDPE                                                                         3.2*                                                       Mitsui Tafmer A-4090 Plastomer                                                                     2.0*                                                       Mitsui Tafmer A-4085 Plastomer                                                                     2.35 (108,000/46,000)                                      Mitsui Tafmer A-1085 Plastomer                                                                     2.00 (160,000/80,000)                                      Matsui Tafmer A-0585                                                                               2.05 (190,000/92,600)                                      Ethylene Alpha Olefin                                                          ______________________________________                                          *Reported by manufacturer in the aforementioned "Proceedings of FuturePak      '91", page 314. Procedure for measuring Mw/Mn not identified.                  **Mw and Mn values are in g/mole.                                        

Melt Index

Melt Index (MI) is a measure of the rate of extrusion of molten resins through a die, and reflects the molecular weight as well as the melt strength of the material. That is, relatively low MI values indicate higher molecular weight-higher melt strength resins. For purposes of this invention, suitable ethylene alpha olefin copolymers for use in forming the invention films have melt index values not exceeding about 1.0 as determined by ASTM D-1238, condition E (2.16 kg weight) at 190° C. As will be apparent from the following Table E (Melt Indices), this means that from the melt index standpoint these suitable ethylene alpha olefins are more similar to previously known VLDPE materials than prior art plastomers.

                  TABLE E                                                          ______________________________________                                         Melt Indices                                                                                      MI (g/10 min per ASTM                                       Type Compound and Manufacturer                                                                    D-1238 Condition E)                                         ______________________________________                                         Union Carbide 1085 VLDPE                                                                          0.8                                                         Union Carbide 1137 VLDPE                                                                          1.0                                                         Union Carbide 1192 VLDPE                                                                          0.19                                                        Union Carbide 1096-2 VLDPE                                                                        0.38                                                        Dow 4001 VLDPE     1.0                                                         Dow XU61520.01 VLDPE                                                                              1.0                                                         Mitsui Tafmer A-4085 Plastomer                                                                    3.6                                                         Mitsui Tafmer A-4090 Plastomer                                                                    3.6                                                         Mitsui Tafmer A-1085 Plastomer                                                                    1.4                                                         Exxon Exact 3027   3.5                                                         Mitsui Tafmer A-0585                                                                              0.5                                                         ______________________________________                                    

Melting Points

There is a substantial difference in melting points between previously known VLDPE and prior art ethylene alpha olefin plastomers. In general, the latter have melting points below about 90° C. whereas prior art VLDPE materials have melting points above about 90° C. The aforementioned EVA (10% vinyl acetate content) has a melting point of 97° C. One ethylene alpha olefin copolymer suitable for use in this invention (Tafmer A-0585) has a relatively low melting point of about 67° C. The melting points of various ethylene alpha olefins and EVA are summarized in Table F.

                  TABLE F                                                          ______________________________________                                         Melting Points (°C.)                                                    Type Compound and Manufacturer                                                                      MP (°C.)                                           ______________________________________                                         Union Carbide 6833 EVA                                                                               97                                                       Union Carbide 1137 VLDPE                                                                            117                                                       Union Carbide 1085 VLDPE                                                                            117                                                       Union Carbide 1063 VLDPE                                                                            124                                                       Union Carbide 1064 VLDPE                                                                            125                                                       Union Carbide 1092 VLDPE                                                                            121                                                       Dow Attane 4001 VLDPE                                                                               121                                                       Dow Attane 4003 VLDPE                                                                               107/124 (two peaks)                                       Mitsui Tafmer A-4085 Plastomer                                                                       71                                                       Mitsui Tafmer A-4090 Plastomer                                                                       85                                                       Mitsui Tafmer A-1085 Plastomer                                                                       71                                                       Mitsui Tafmer A-0585 Ethylene                                                                        67                                                       Alpha Olefin                                                                   ______________________________________                                    

Ethylene alpha olefins suitable for use as the primary thermoplastic polymer in the film of this invention have a melting point below about 100° C. Higher melting polymers do not provide the ultra high shrink characteristic of the inventive film.

Vicat Softening Point

With the exception of Union Carbide's type 1085 material, previously known VLDPE materials tend to be less flexible and harder to penetrate than prior art plastomer-type ethylene alpha olefins, which tend to be more flexible and softer. In this regard at least one ethylene alpha olefin useful in the practice of this invention (Mitsui's Tafmer A-0585) is more similar to most prior art ethylene alpha olefin plastomers than previously known VLDPE materials. This is illustrated by comparing Vicar softening points for the various materials.

In a preferred embodiment of ethylene alpha olefin copolymers suitable for manufacture of the inventive film, its Vicar softening point is less than about 70° C. as measured in accordance with ASTM 1525. By this procedure, Vicar softening point is the temperature at which a flat-ended needle of 1-mm² circular cross section will penetrate a thermoplastic specimen to a depth of 1 mm under a specified load using a selected uniform rate of temperature rise. Vicat softening points for various ethylene alpha olefins have been reported by the resin manufacturers and are summarized in Table G as follows.

                  TABLE G                                                          ______________________________________                                         Vicat Softening Point                                                          Type Compound and Manufacturer                                                                    VSP (°C.) per ASTM-1525                              ______________________________________                                         Union Carbide 1085 VLDPE                                                                          45                                                          Union Carbide 1137 VLDPE                                                                          80                                                          Union Carbide 1063 VLDPE                                                                          93                                                          Union Carbide 1064 VLDPE                                                                          90                                                          Union Carbide 1569 VLDPE                                                                          94                                                          Dow Attane 4001 VLDPE                                                                             95                                                          Dow Attane 4003 VLDPE                                                                             80                                                          Dow Attane 4004 VLDPE                                                                             92                                                          Mitsui Tafmer A-1085 Plastomer                                                                    58                                                          Mitsui Tafmer A-4085 Plastomer                                                                    54                                                          Mitsui Tafmer A-4090 Plastomer                                                                    65                                                          Mitsui Tafmer A-20090 Plastomer                                                                   60                                                          Mitsui Tafmer A-0585                                                                              62                                                          Ethylene Alpha Olefin                                                          ______________________________________                                    

Tensile Properties

One of the characteristics of ethylene alpha olefins useful in the practice of this invention is the ability to absorb tensile stresses without rupturing. In particular the density should be between about 0.88 and about 0.905 g/cm², so that stresses are absorbed in the more numerous short chain branches present in the relatively high alpha olefin comonomer content of the copolymer. On the other hand, lower density resins are too rubbery for processing into a biaxially stretched film.

Another important property for characterizing suitable ethylene alpha olefin copolymers is its Young's Modulus, sometimes referred to as the modulus of elasticity, and associated with a polymer undergoing tensile deformation. It is the ratio of stress to strain below the proportional limit of a material. Stated otherwise, it is the stiffness or a measure of the resistance to tensile deformation that a polymer exhibits when a tensile stress is applied. Stiff materials have high values whereas low to moderate values indicate more elasticity and flexibility. For purposes of this invention, suitable ethylene alpha olefins have a Young's Modulus below about 750 kg/cm². These materials, like the prior art ethylene alpha olefin plastomers, can absorb more of the energy imparted by a projectile, leading to higher values of dynamic puncture. Also, their elasticity allows them to be biaxially stretched to a higher extent, leading to higher shrink in films. Mitsui, a manufacturer of ethylene alpha olefin plastomers, Tafmer A-0585 and previously known VLDPE materials, reports the following values for Young's Modulus as summarized in Table H.

                  TABLE H                                                          ______________________________________                                         Young's Modulus                                                                Material           Kg/cm.sup.2                                                 ______________________________________                                         Tafmer A-0585      400                                                         Tafmer A-4085*     400                                                         Tafmer A-20090*    600                                                         VLDPE (0.896 density)**                                                                           800                                                         VLDPE (0.907 density)**                                                                           1820                                                        ______________________________________                                          *"Tafmer" publication of Mitsui Petrochemical Ind., Ltd., page 12              **"Proceedings of FuturePak '91", page 314                               

From Table H, one would expect Tafmer A-0585 (like the prior art Tafmer-type ethylene alpha olefin plastomers), to be too weak to form monolayer biaxially stretched heat shrinkable films therefrom. It was in fact quite surprising that this could be done with Tafmer A-0585 to produce such film with commercially acceptable tensile strength properties and very high puncture resistance.

Shrinkage

The biaxially stretched film of the present invention are "heat-shrinkable", and as used herein this means the film has an unrestrained shrinkage of at least 50 percent in at least one of the machine and transverse directions at 90° C. Shrinkage values are obtained by measuring unrestrained shrink of the stretch film at 90° C. for five seconds. Four test specimens are cut from a given sample of the stretched film to be tested. The specimens are cut to 10 cm in the machine direction by 10 cm in the transverse direction. Each specimen is completely immersed for 5 seconds in a 90° C. water bath. The distance between the ends of the shrunken specimen is measured. The difference in the measured distance for the shrunken specimen and the original 10 cm is multiplied by ten to obtain the percent of shrinkage for the specimen. The shrinkage for the four specimens is averaged for the MD shrinkage values of the given film sample, and the shrinkage for the four specimens averaged for the TD shrinkage value.

The films of this invention are generally prepared from dry resins which are melted in an extruder and passed through a die to form the primary film material, most commonly in a tube form.

The well-known two step "double bubble" or trapped bubble process may be used to prepare the film of this invention (either monolayer or multilayer). One embodiment of this process is described in Pahlke U.S. Pat. No. 3,456,044. In this Pahlke-type double bubble process a primary tube is prepared, cooled, reheated and the tube is simultaneously stretched in the machine direction ("MD") by operating longitudinally spaced nip rolls at different speeds, and in the transverse direction ("TD") by inflating air inside the tube. Suitable stretch ratios are from about 2 to about 6 with ratios of about 3 to about 5 preferred. The multilayer heat-shrinkable, puncture resistant biaxially stretched thermoplastic films of this invention may be formed into a primary tube by known techniques such as by coextruding at least the core layer and the first and second outer layers on each side of the core layer to form a primary tube as for example described in Canadian Patent No. 982923. Alternatively, the composite primary tube may be formed by coating lamination, wherein a first outer tubular layer is extruded and thereafter the core and second outer tubular layers are sequentially coated onto the outer surfaces of the first tubular layer and the core layer. As another alternative, the first outer and core outer layers may themselves be coextruded, and the second outer layer thereafter coated onto the outside surface of the core layer. Coating lamination procedures are described in Brax et al U.S. Pat. No. 3,741,253. As still another alternative, the at least three layer film may be formed as a sheet by the well-known slot casting procedure.

The preferred method for forming the films of this invention (both monolayer and multilayer) is coextrusion of a primary tube which is then biaxially oriented in the manner described in the aforementioned Pahlke Patent. In the following multilayer film Examples 2-5, all three layers were coextruded and the primary tube was cooled. It was then reheated to the draw temperature for biaxial orientation.

Although not essential in the practice of this invention, it may be desirable to cross-link a monolayer film embodiment or one or more layers of a multilayer embodiment of the inventive film for improvement of abuse and/or puncture resistance and other physical characteristics. This for example may be accomplished by irradiation using high energy electrons, ultra violet radiation, x-rays, beta particles and the like. The irradiation source can be any electron beam generator operating in a range of about 150 kilovolts to about 6 megavolts with a power output capable of supplying the desired dosage. The voltage can be adjusted to appropriate levels which may be for example 1 to 6 million volts or higher or lower. Many apparatus for irradiating films are known to those skilled in the art. The irradiation is usually carried out at a dosage up to about 20 MR, typically between about 1 MR and about 20 MR, with a preferred dosage range of about 2 MR to about 12 MR. Irradiation can be carried conveniently at room temperature, although higher and lower temperatures, for example, 0° C. to 60° C. may be employed.

Processwise, irradiation can be applied to a single substrate layer such as the first outer layer and prior to biaxial stretching if the primary multilayer film is prepared by coating lamination. This type of irradiative cross-linking is for example described in the aforementioned Brax et al U.S. Pat. U.S. 3,741,253. Alternatively, if the entire film is simultaneously coextruded it may be preferable to irradiate the entire multilayer film, and for maximum efficiency this should be done after biaxial stretching at a dosage level below about 8 MR, as for example described in Lustig et al U.S. Pat. No. 4,737,391.

Cross-linking may also be accomplished chemically through utilization of peroxides, as is well known to those skilled in the art. A general discussion of cross-linking can be found at pages 331 to 414 of volume 4 of the Encyclopedia of Polymer Science and Technology, Plastics, Resins, Rubbers, Fibers published by John Wiley & Sons, Inc. and copyrighted in 1966. This document has a Library of Congress Catalog Card Number of 64-22188.

Unless otherwise noted, the resins utilized in the present invention are generally commercially available in pellet form and, as generally recognized in the art, may be melt blended or mechanically mixed by well-known methods using commercially available equipment including tumblers, mixers-or blenders. Also, if desired, well known additives such as processing aids, slip agents, antiblocking agents and pigments, and mixtures thereof may be incorporated into the film, by blending prior to extrusion. The resins and any additives are introduced to an extruder (generally one extruder per layer) where the resins are melt plastified by heating and then transferred to an extrusion (or coextrusion) die for formation into a tube. Extruder and die temperatures will generally depend upon the particular resin or resin containing mixtures being processed and suitable temperature ranges for commercially available resins are generally known in the art, or are provided in technical bulletins made available by resin manufacturers. Processing temperatures may vary depending upon other process parameters chosen.

In extrusion of monolayer films according to this invention, extruder barrel and die temperatures may be as high as the melting point of the ethylene alpha olefin being processed. However depending upon such factors as other resins which may be employed, the manufacturing process used and particular equipment and other process parameters utilized, variations are expected. Actual process parameters including process temperatures will be set by one skilled in the art without undue experimentation. For example, in the 100% Tafmer A-0585 sample 3 the extruder barrel temperature range was about 350°-360° C. and the die temperature was about 400° C.

Advantageously, a preferred embodiment of the inventive heat-shrinkable film will have a maximum extractable portion of 5.5 percent by weight of polymer in n-hexane at 50° C. for 2 hours as further described below. This 5.5 weight percent represents the desired maximum n-hexane extractable limit for olefin copolymers of the type employed by the present invention for use in articles that contact food except for articles used for packing or holding food during cooking. Beneficially, the maximum extractable portion as described above will be 2.6 percent in an especially preferred embodiment of the inventive film suitable or use in articles used in packing or holding food during cooking. The above maximum extractable values correspond to current limits for a class of resins intended for use in contact with food as set forth and described by the U.S. Food & Drug Administration in 21 CFR 177.1520 (which description is hereby incorporated in its entirety by reference). Mitsui, the manufacturer of Tafmer products, advises that these products meet these extractable limits (in the film surface contacting food) if Tafmer comprises no more than 40 % of a blend with EVA or certain polyethylenes.

In all of the following examples, all films were prepared by the double or trapped bubble method as broadly described in the aforementioned Pahlke U.S. Pat. No. 3,456,044. In the multilayer embodiments of Examples 2-5, all three layers were simultaneously coextruded, cooled and then reheated for biaxial orientation. The VLDPE used was the aforedescribed Attane XU 61520.01 or 4001, both manufactured by the Dow Chemical Company of Midland, Mich., and comprising an ethylene and 1-octene copolymer with a density of about 0.912 gm/cc. The EVA was Union Carbide Corporation's type 6833 with 10 wt.% vinyl acetate content.

The extrusion-biaxial stretching equipment used in Examples 1-3 was laboratory (small) scale whereas the extrusion equipment used in Examples 4 and 5 was commercial size (large scale).

EXAMPLE 1

In Example 1, six different pure component resins were used in attempts to manufacture heat shrinkable biaxially stretched monolayer films in tube form, and three of the runs were successful. Five of these resins were included for comparison with film of this invention, ie. sample 1 (Tafmer A-4085), sample 2 (Tafmer A-1085), sample 4, (Exxon's Exact 3027), sample 5 (EVA) and sample 6 (Dow's type 61520.01 VLDPE). Sample 3 (Tafmer A-0585) is an ethylene alpha olefin suitable for manufacturing film of this invention. Tafmer types A-4085 and A-1085 have already been described as prior art ethylene alpha olefin plastomers.

Exact 3027 is an ethylene-butene copolymer manufactured by Exxon Chemical Company using a homogeneous metallocene single-site catalyst system. It is reported by the manufacturer as having a melt index of 3.5 (2 kg at 190° C.), density of 0.900 gms/cc, a single melting point of about 92° C., and an Mw/Mn of about 2. Exxon classifies its Exact materials with densities of at least about 0.900 gm/cc as VLDPE.

The films were all prepared in the same extrusion-orientation system of the general type disclosed in the aforementioned Pahlke Patent. The primary tube was about 21/2 inches flat width inside diameter, and final heating to the draw temperature was by an air cushion which had itself been heated by transverse flow through a heated porous tube concentrically positioned around the moving primary tube. The final tube was about 12 inches inside diameter and the film thicknesses were about 2 mils.

Physical properties of the resulting monolayer films were measured and are summarized in Table I.

                                      TABLE I                                      __________________________________________________________________________     Monolayer Nonirradiated Films                                                                Sample No.                                                               Units 1       2       3       4       5       6                        __________________________________________________________________________     Formulation   100% Tafmer                                                                            100% Tafmer                                                                            100% Tafmer                                                                            100% Exact                                                                             100% EVA                                                                               100% VLDPE                             A-4085  A-1085  A-0585  3027    (UCC-6833)                                                                             (Dow 61520.01)           Tensile psi   Could   Could   7318/8691                                                                              Could   7474/11330                                                                             13258/15463              Strength,     Not     Not             Not                                      MD/TD         Form    Form            Form                                     Elongation                                                                             %     Film    Film    202/180 Film    190/210 235/227                  at break,     From    From            From                                     MD/TD         Resin   Resin           Resin                                    Shrink  %                     68/63           30/48   18/31                    @90° C.,                                                                MD/TD                                                                          Dynamic cmkg/mil              11.5            2.47    2.90                     Puncture                                                                       Hot Water                                                                              sec.                  .sup.(1)        33.6/120+                                                                              120+/120+                Puncture                                                                       (metal/wood                                                                    probe @                                                                        95° C.)                                                                 Haze    %                     4.3             1.7     2.8                      Gloss   H.U.                  77.4            89.2    87.8                     __________________________________________________________________________      .sup.(1) Melts at 67° C.                                          

Referring now to Table I, sample 1 (100% Tafmer A-4085), sample 2 (100% Tafmer A-1085) and sample 4 (100% Exact 3027) could not be formed into film tubes, yet sample 3 (100% Tafmer A-0585) formed a heat shrinkable biaxially stretched film with outstanding physical properties. This will be apparent from a comparison with the physical properties of sample 5 (100% EVA - 10% vinyl acetate) and sample 6 (100% VLDPE - 0,912 density) heat shrinkable biaxially stretched films.

More specifically, even though the physical properties of Tafmer A-4085, Tafmer A-1085 and Tafmer A-0585 resins are very similar, it was unexpectedly discovered that a monolayer heat shrinkable biaxially stretched film with uniquely advantageous physical properties (relative to other ethylene alpha olefin copolymers) only could be prepared from Tafmer A-0585. For example, its tensile strength and elongation characteristics are at commercially acceptable levels, yet its shrink properties far surpass those of 100% EVA. This was very surprising because EVA has been generally recognized as providing the highest biaxial shrink properties of widely used ethylene copolymers. Moreover the dynamic puncture resistance of 100% Tafmer A-0585 sample 3 was unexpectedly several times higher than 100% VLDPE sample 6. This was unexpected from a comparison of their resin physical properties, and particularly since prior art polyethylene films of this general type have been recognized by those skilled in the art as providing the highest strength properties of ethylene alpha olefinbased heat shrinkable biaxially stretched films. Sample 3 demonstrates a preferred monolayer embodiment having puncture strength of at least about 10 cmkg/mil. It should be noted, however, that because of its relatively low melting point (67° C.), 100% Tafmer A-0585 film is not suitable for systems wherein the film is heat shrunk by contact with boiling water. Also, its optical properties are somewhat inferior to the prior art film samples 5 and 6.

It is believed that the reasons why heat shrinkable biaxially oriented monolayer film can be prepared from Tafmer A-0585 but not from Tafmer A-4085 or Tafmer A-1085 or Exact 3027 are the aforedescribed differences in melt index and possibly Mw and Mn. Compared to prior art VLDPE, the remarkably higher shrink and dynamic puncture values are believed due to differences in density, melting point, Mw/Mn, and possibly Mw and Mn. Finally compared to EVA sample film 5, the much high shrink performance of invention film sample 3 is believed in part due to its greater elasticity.

Table I demonstrates that monolayer films of this invention are unexpectedly superior to prior art films used in shrink packaging food products wherein an oxygen barrier is not required, eg. poultry such as chicken. Accordingly, with acceptably low n-hexane extractables these films would also be suitable for such end uses.

EXAMPLE 2

In Example 2, four nonirradiated multilayer films (samples 7-10) were prepared each with a vinylidene chloride copolymer-type core layer sandwiched between two identical outer layers. All films were the heat shrinkable biaxially stretched type of about 2.0 mils overall thickness. One outside layer (the inner layer of the tube which would become the inner and heat-sealing layer of bags formed from the tube) was about 1.2 mils thick. The other outside layer (the outer layer of the tube which would become the outer abuse-resistant layer of bags formed from the tube) was about 0.6 mils thick. The purpose of Example 2 was to compare physical and optical properties of three layer films of the oxygen barrier core layer type prepared in a small scale extrusion-biaxial stretching system. In these films the outer layers are formed of blends including ethylene alpha olefin compositions according to this invention (samples 8-10), and a prior art commercially employed VLDPE-EVA blend (sample 7) used as the control.

The films were all prepared in the same small scale-orientation system of the general type described in the Pahlke Patent. The extruder barrel and die temperatures were about 320-330° C. The primary tube was about 41/8 inch inside diameter and the final biaxially stretched tube was about 19 inches inside diameter.

Physical and optical properties of the resulting nonirradiated three layer films were measured and are summarized in Table J.

                                      TABLE J                                      __________________________________________________________________________     Three Layer Films.sup.(2) - Nonirradiated and Small Scale                                       Sample No.                                                               Units 7       8        9       10                                   __________________________________________________________________________     Formulation.sup.(1)                                                                       weight                                                                               70.6%   69.1% Tafmer                                                                            40% Tafmer                                                                             55% Exact                            of Outer Layers  Dow 4001,                                                                              A-0585,  A-0585, 0633,                                                 VLDPE   22.5% EVA                                                                               33% Exact                                                                              40% Tafmer                                            25.0% EVA        0633,   A-0585                                                                 23% EVA                                      Tensile    psi   12430/12228                                                                            15592/12075                                                                             11640/12102                                                                            15505/10223                          Strength, MD/TD                                                                Elongation at                                                                             %     173/184 180/256  206/208 178/220                              break, MD/TD                                                                   Shrink @90° C.,                                                                    %     23/33   56/52    44/46   53/48                                MD/TD                                                                          Shrink Force @                                                                            g/mil 131/178 80/60    123/109 146/80                               90° C. MD/TD                                                            Dynamic    cmkg/mil                                                                             2.5     8.0      4.7     7.9                                  Puncture                                                                       Hot Water  sec.  19.8/-- 4.8/1.5  6.9/2.4 115+/2.2                             Puncture                                                                       (wood/metal                                                                    probe @ 95° C.)                                                         Haze       %     8.6     5.7      2.2     2.4                                  Gloss      H.U.  70.8    72.1     92.4    90.9                                 __________________________________________________________________________      .sup.(1) Difference between 100% and reported total is processing aid(s).      .sup.(2) Oxygen barriercore layer is a blend of 85% vinylidene                 chloridemethyl acrylate and 15% vinylidene chloridevinyl chloride              copolymers.                                                              

Summarizing Table J, samples 8 and 10 are embodiments of the invention and may be compared with sample 7, a heat shrinkable biaxially stretched film used after irradiation and in bag form for packaging fresh red meat and processed meats. Since it contains about 70% type 4001 VLDPE, sample 8 (69.1% Tafmer A-0585) may be directly compared with control sample 7 because in each instance the balance of the composition is primarily EVA plus a small percentage of processing aids. Invention sample 8 has substantially higher MD tensile strength and dynamic puncture strength than prior art sample 7, although its hot water puncture value was relatively low because of the low Tafmer A-0585 melting point. The severalfold higher dynamic puncture value for this embodiment of the invention was surprising because, as previously stated, prior art VLDPE is known to provide the highest puncture resistance to the ethylene alpha olefin copolymer type inner and outer layers of state-of-art multilayer oxygen barrier type films. Also, the invention sample 8 MD and TD shrink properties were far superior to prior art sample 7. The former's optical properties were slightly better than prior art sample 7. These improvements are believed to be related to differences in density, Mw/Mn, possibly Mw and Mn, melting point and Young's Modulus.

Samples 9 (40% Tafmer A-0585, 33% Exact 0633, and 23% EVA) and 10 (55% Exact 0633 and 40% Tafmer A-0585) demonstrate that physical properties may be adjusted by blending the ethylene alpha olefin copolymer of this invention either in a two component blend with another ethylene alpha olefin (Exact 0633), or in a three component blend with another ethylene alpha olefin and at least one other constituent such as EVA. Exact 0633 is an ethylene alpha olefin copolymer manufactured by Exxon Chemical Company using a homogeneous metallocene singlesit catalyst system.

More particularly, sample 9 provides higher shrink force, hot water puncture and superior opticals relative to 69% Tafmer A-0585 sample 9, by replacing some of the Tafmer A-0585 with Exact 0633. However, the tensile strength, shrink and dynamic puncture values are made somewhat lower by the substitution. The sample 9 shrink could for example be increased to the about 50% threshold of this invention by using a slightly higher Tafmer A-0585 concentration. Sample 10 demonstrates that a two component blend provides the best balance of all Table I invention embodiments. Accordingly, one preferred embodiment of this invention involves use of a blend comprising the aforedescribed ethylene alpha olefin copolymer, and another ethylene alpha olefin copolymer prepared by a metallocene single site catalyst.

Table J shows that with respect to nonirradiated multilayer films prepared in small scale equipment, the three layer-oxygen barrier core type with the present ethylene alpha olefin copolymer in the inner and outer layers are superior in terms of certain physical properties to comparable prior art films currently used for shrink packaging fresh red meat and processed meat. Since the other physical properties of these inventive films are commercially acceptable, they are also suitable for these end uses. This of course presumes that if the film is intended for direct contact with food it will satisfy the n-hexane extractable limit. As will be discussed below in more detail in connection with Example 3, the physical properties of the nonirradiated Tafmer A-0585 and Exact 0633 blend sample 10 is actually superior to its irradiated counterpart. Accordingly, in some end uses where the evacuated packages are sealed by clipping or where the sample 10 inner layer heat seal temperature range is adequate, irradiation may be avoided.

EXAMPLE 3

In Example 3, four irradiated multilayer films (samples 11-14) were prepared each with a vinylidene chloride copolymer-type oxygen barrier core layer sandwiched between two identical outer layers. All films were the heat shrinkable biaxially stretched type of about 2.0 mils overall thickness. The heat sealing outer layer was about 1.2 mils thick and the abuse-resistant outer layer was about 0.6 mils thick.

The purpose of Example 3 was to compare physical and optical properties of irradiated three layer films of the oxygen barrier core layer type. In these films the outer layers are formed of blends including ethylene alpha olefin compositions according to this invention (samples 12-14) and a prior art commercially employed VLDPE-EVA blend (sample 11) used as the control.

The same small scale extrusion-orientation system was used to prepare each of samples 11-15, and it was the same system used in Example 2. The biaxially stretched films were irradiated to about 4 MR (after orientation) in the manner described in Lustig et al U.S. Pat. No. 4,737,391.

Physical and optical properties of the resulting irradiated three layer films were measured and are summarized in Table K.

                                      TABLE K                                      __________________________________________________________________________     Three Layer Films.sup.(2) - Irradiated.sup.(3) and Small Scale                                  Sample No.                                                               Units 11      12      13      14                                    __________________________________________________________________________     Formulation.sup.(1) of                                                                    weight                                                                               70.6%   40% Tafmer                                                                             55% Exact                                                                              69.1% Tafmer                          Outer Layers     Dow 4001                                                                               A-0585, 0633,   A-0585.                                                VLDPE   33% Exact                                                                              40% Tafmer                                                                             22.5% EVA                                              25.0% EVA                                                                              0633,   A-0585                                                                 23% EVA                                               Tensile Strength,                                                                         psi   13070/13035                                                                            14233/12085                                                                            15210/12725                                                                            15223/12182                           MD/TD                                                                          Elongation at                                                                             %     185/202 174/212 159/202 161/301                               break, MD/TD                                                                   Shrink @90° C.,                                                                    %     22/32   40/42   49/44   61/46                                 MD/TD                                                                          Shrink Force @                                                                            g/mil 111/173 131/109 149/96  85/31                                 90° C. MD/TD                                                            Dynamic Puncture                                                                          cmkg/mil                                                                             2.62    3.48    4.23    5.48                                  Hot Water  sec.  120+/20.4                                                                              120+/101                                                                               120+/120+                                                                              --                                    Puncture                                                                       (wood/metal probe                                                              @ 95° C.)                                                               Haze       %     7.9     3.0     3.4     3.5                                   Gloss      H.U.  73.2    85.0    83.6    82.1                                  __________________________________________________________________________      .sup.(1) Difference between 100% and reported total is processing aid(s).      .sup.(2) Oxygen barriercore layer is a blend of 85% vinylidene                 chloridemethyl acrylate and 15% vinylidene chloridevinyl chloride              copolymers.                                                                    .sup.(3) Irradiation dose is 4 MR.                                       

Summarizing Table K, samples 12-14 are embodiments of the invention and may be compared with sample 11, an irradiated heat shrinkable biaxially stretched film used in bag form for packaging fresh red meat and processed meats. Since control sample 11 contains about 70% type 4001 VLDPE, sample 14 (Tafmer A-0585) may be directly compared because in each instance the remainder is primarily EVA and a small amount of processing aids. Sample 14 has substantially higher tensile strength and shrink in both directions. Moreover, the dynamic puncture resistance of sample 14 is about twice that of control sample 11. Finally, the optical properties of sample 14 are superior to control sample 11.

Sample 14 illustrates a preferred embodiment of this invention comprising an irradiated biaxially stretched film with three layers. They include a vinylidene chloride-methyl acrylate copolymer oxygen barrier-core layer and an outer layer on each side of the barrier-core layer. The outer layers each comprise a blend of between about 65% and 75% of the selected ethylene alpha olefin, and between about 20 and 30% ethylene vinyl acetate. The film is heat shrinkable at least about 55% in both the machine and transverse directions at 90° C. It preferably has dynamic puncture strength of at least about 3 cmkg/mil.

Improvements over the control sample 11 are also achieved by substituting a different ethylene alpha olefin copolymer (Exact 0633) for a portion of the ethylene alpha olefin of this invention to form a three component blend (sample 12), or using a two component blend of Exact 0633 and Tafmer A-0585 in the inner and outer layers (sample 13). The latter, comprising 40% Tafmer A-0585 and 55% Exact 0633, provides the best balance of physical properties among samples 12-14. However, comparison of physical properties with nonirradiated sample 10 (Table J) having the same composition suggests that since the irradiated film properties are inferior, irradiation should only be employed if needed to broaden the heat sealing range of the inner layers and improve the hot water puncture resistance.

Since the control prior art film is commercially used to shrink package fresh red meat and processed meat and the invention film samples have certain improved physical properties compared to this prior art film and the remaining physical properties are commercially acceptable, these film embodiments of the invention are suitable for the same end use.

EXAMPLE 4

In Example 4, four nonirradiated biaxially stretched and heat shrinkable multilayer films (samples 15-18) were prepared, each with a vinylidene chloride copolymer-type oxygen barrier core layer sandwiched between two identical outer layers. All films were the heat shrinkable biaxially stretched type of about 2 mils overall thickness. The heat sealing outer layer was about 1.2 mils thick and the abuse-resistant outer layer was about 0.6 mils thick. Samples 15 (Dow type XU 61520.01 VLDPE-EVA blend outer layers) 17 (100% Dow type 4001 VLDPE outer layers) and 18 (100% EVA outer layers) are film compositions commercially used in the irradiated form for meat packaging. Sample 16 (Exact 0633-Tafmer A-0585 blend) is an embodiment of this invention.

A large scale extrusion-biaxial stretching system of the Pahlke Patent type was used to prepare samples 15-18. The primary tube was about 2 inches inside diameter flat width whereas the final biaxially stretched tube flat width was about 10 inches inside. Final heating to the draw temperature was by an air cushion which had itself been heated by transverse flow through a heated porous tube concentrically positioned around the moving primary tube.

The purpose of Example 4 was to compare physical and optical properties of nonirradiated three layer films of the oxygen barrier core layer type, prepared in a large scale commercial type extrusion-biaxial stretching system.

Physical and optical properties of the resulting nonirradiated three layer film were measured and are summarized in Table L.

                                      TABLE L                                      __________________________________________________________________________     Three Layer Films.sup.(2) - Nonirradiated and Large Scale                                          Sample No.                                                               Units 15      16       17        18                              __________________________________________________________________________     Formulation.sup.(1) of                                                                       weight                                                                               69.1%   56.0% Exact                                                                             100% VLDPE.sup.(4)                                                                       100% EVA                        Outer Layers        VLDPE.sup.(3)                                                                          0633,                                                                  22.5% EVA                                                                              40.0% Tafmer                                                                   A-0585                                             Film Thickness                                                                               mil   2.07    2.62     2.5       2.10                            Tensile Strength,                                                                            psi   16068/14508                                                                            15130/14685                                                                             14498/15475                                                                              9384/11338                      MD/TD                                                                          Elongation at %     215/200 267/208  198/174   134/158                         break, MD/TD                                                                   Shrink @90° C., MD/TD                                                                 %     28/39   57/60    24/36     40/50                           Shrink Force @ 90° C.                                                                 g/mil 150/195 143/152  --        143/145                         MD/TD                                                                          Dynamic Puncture                                                                             cmkg/mil                                                                             2.13    7.23,8.36                                                                               3.27      1.71                            Hot Water Puncture                                                                           sec.  120+/50.4                                                                              18.6/8.4 27.0      120+                            (wood/metal probe                                                              @95° C.)                                                                Haze          %     6.4     3.9      2.8       4.5                             Gloss         H.U.  74.7    84.6     90.9      82.0                            Tear Strength MD/TD                                                                          gm/mil                                                                               27/33   61/51    --        --                              __________________________________________________________________________      .sup.(1) Difference between 100% and reported total is processing aid(s).      .sup.(2) Oxygen barriercore layer is a blend of 85% vinylidene chloride        methyl acrylate and 15% vinylidene chloridevinyl chloride copolymers           .sup.(3) Dow type XU 61520.01 VLDPE                                            .sup.(4) Dow type 4001 VLDPE.                                            

Referring now to Table L, sample 16 (56.0% Exact 0633-40.0% Tafmer A-0585) is an invention embodiment whereas samples 15 (69% VLDPE and 22.5% EVA), 17 (100% VLDPE) and 18 (100% EVA) are prior art films. Sample 16 demonstrates that certain improvements in physical properties over comparable prior art film may be realized by using two component blends of the present ethylene alpha olefin copolymer of this invention and another ethylene alpha olefin copolymer prepared by a metallocene single site catalyst system, in the inner and outer layers. In particular, sample 16 has the highest shrink in both directions as well as the highest dynamic puncture value of all film samples in this test series. Its optical properties were nearly as good as the best prior art film from this standpoint (sample 17).

EXAMPLE 5

In Example 5, five irradiated multilayer films (samples 19-23) were prepared with a vinylidene chloride copolymer-type oxygen barrier core layer sandwiched between two identical outer layers. The overall thickness of the films was about 2 mils, the heat sealable outer layer thickness was about 1.2 mils and the abuse-resistant outer layer was about 0.6 mils thick. Sample 19 (Dow XU 61520.01 type VLDPE-EVA blend outer layers) is commercially used for meat packaging and is the control film. Samples 20, 21 and 22 have outer layers containing Tafmer A-0585 and are embodiments of this invention. All films were post-irradiated to about 4 MR in the manner generally described in previously referenced Lustig et al Patent '391.

The same large scale extrusion-orientation system used in Example 4 was used in Example 5. That is, the primary tube inside diameter was about 2 inches and the biaxially stretched tube diameter was about 10 inches.

The purpose of Example 5 was to compare physical and optical properties of invention embodiments with prior art irradiated three layer films of the oxygen barrier core layer type commercially used for shrink packaging of meat, wherein the films were prepared in a large scale commercial type extrusion-biaxial stretching system.

Physical and optical properties of the resulting irradiated three layer were measured and are summarized in Table M.

                                      TABLE M                                      __________________________________________________________________________     Three Layer Films - Irradiated.sup.(1) and Large Scale                                            Sample No.                                                               Units 19     20     21        22           23                     __________________________________________________________________________     Formulation of Outer                                                                        weight                                                                               69.1%  70% Tafmer                                                                            55% Exact 0633,                                                                          40% Tafmer A-0585,                                                                          100% EVA               Layers             VLDPE.sup.(2)                                                                         A-0585,                                                                               40% Tafmer A-0585                                                                        Exact 0633, 23%                                                                             6833                                      22.5% EVA                                                                             25% EVA                                              Tensile Strength, MD/TD                                                                     psi   --     10088/11380                                                                           9627/7688 9627/7688    10000/12000            Elongation at break,                                                                        %     --     177/196                                                                               191/146   191/146      132/192                MD/TD                                                                          Shrink @90° C., MD/TD                                                                %     26/35  58/59  57/58     57/58        33/46                  Dynamic Puncture                                                                            cmkg/mil                                                                             2.4    3.3    3.1       3.1          2.1                    Hot Water Puncture                                                                          sec.  --     3.6    4.2       4.2          --                     (metal probe @ 90° C.)                                                  Haze         %     6.9    9.6    9.3       9.3          6.8                    Gloss        H.U.  81.8   68.9   64.6      64.6         76.6                   __________________________________________________________________________      .sup.(1) All films were irradiated at 4 MR.                                    .sup.(2) Dow XU 61520.01 type VLDPE.                                     

Referring now to Table M, invention film sample 20 may be compared with control sample 19 because each has about 69% ethylene alpha olefin copolymer. In each instance the balance of the composition is primarily EVA with a small percentage of processing aids. The dynamic puncture strength of sample 20 is substantially higher than sample 19.

With respect to shrink, invention film sample 20 is far superior to previously known VLDPE sample film 19, and in fact superior to 100% EVA inner-outer layer film sample 23. As previously explained, this was surprising because EVA is known in the art as providing the best shrink of commercially used ethylene copolymer inner and outer layer type oxygen barrier multilayer films. Sample 20 demonstrates a preferred embodiment of the invention wherein the film shrinks at least 55% in both the machine and transverse directions at 90° C.

Invention film sample 21 (55% Exact 0633 and 40% Tafmer A-0585) demonstrates that a two component blend of the ethylene alpha olefin copolymer of this invention and another ethylene alpha olefin (Exact 0633) in the inner and outer layers provides substantially higher shrink than the best performing comparable prior art film (100% EVA sample 23).

Invention film embodiment sample 22 demonstrates that a three component blend of 40% Tafmer A-0585, 33% Exact 0633 and 23% EVA provides certain improved physical properties. For example, its shrink (in both directions) is substantially higher than the best performing prior art film (100% EVA sample 23). Also, its dynamic puncture strength is substantially higher than the best performing prior art film (69.1% previously known VLDPE sample 19). However, its optical properties are somewhat inferior.

Since the control films are commercially used to package fresh red meat and processed meat, and the Table M invention embodiments are superior in terms of certain physical properties and commercially acceptable with respect to the remaining physical properties, the latter are also suitable for the same end use if they satisfy n-hexene extractable limits.

In the Example 2-5 comparisons with films prepared from previously known VLDPE, the latter's density was about 0.912 g/cm³. Lower density VLDPE materials are also commercially available and provide films with relatively higher shrink values than a higher density VLDPE prepared from the same alpha olefin comonomer, eg. C8. The basic reason for this difference is that lowering density increases film flexibility. However, their shrink and puncture strength properties are inferior to the previously described invention embodiments. Accordingly, previously known lower density VLDPE materials such as those of about 0,910 g/cm³ and below (and having melt indices on the order of about 1.0 g/10 min and below), cannot be used to prepare films having properties equivalent to the films of this invention.

This was demonstrated in a series of three layer film tests wherein the barrier layer was identical to the Examples 2-5 films and the outer layers comprised about the same percentages of previously known VLDPE (approximately 70%) and EVA (25% Union Carbide type 6833) as in several samples of Examples 2-5. The control film of these tests included the same 0.912 density Dow type 4001, used for example in previously described samples 7 and 15. Two other previously known VLDPE materials were used: Dow's type XU 61512.21 having 0.901 g/cm³ density and 1.0 g/10 min melt index, and Dow's type XU 61509.32 having 0,911 g/cm³ density and 0.5 melt index. In each instance the comonomer was octene-1.

EXAMPLE 6

In Example 6, four nonirradiated heat shrinkable multilayer film samples 24-27 were prepared by the previously described coextrusion-type double bubble process in laboratory (small) scale equipment. In each instance the primary tube was about 3.25 inches flat width inside diameter, the final tube was about 13 inches inside diameter and the film thicknesses were about 2 mils. Physical and optical properties of these films were measured and the results are summarized in Table N. The latter shows that sample 27 (0.901 density previously known VLDPE) provides substantially higher heat shrink than samples 24 and 25 (0.912 density previously known VLDPE). As previously explained, this was because of the greater flexibility afforded by lower density material. However, lower density VLDPE sample 27 also has substantially lower dynamic puncture strength than the highest performing 0.912 density VLDPE sample 24. The shrink and dynamic puncture strength characteristics of 0.911 density VLDPE sample 26 are substantially the same as 0.912 density VLDPE sample 24.

                                      TABLE N                                      __________________________________________________________________________     Low Density VLDPE Three Layer Films                                            Nonirradiated and Small Scale                                                                    Sample No.                                                                Units                                                                               24        25        26        27                             __________________________________________________________________________     Formulation of                                                                              weight                                                                              70.6% VLDPE.sup.(1)                                                                      70.6% VLDPE.sup.(1)                                                                      70.6% VLDPE.sup.(2)                                                                      70.6% VLDPE.sup.(3)            Outer Layers      25.0% EVA 25.0% EVA 25.0% EVA 25.0% EVA                      Tensile Strength,                                                                           psi  12330/12815                                                                              13070/13035                                                                              13157/12980                                                                              11040/12435                    MD/TD                                                                          Elongation at                                                                               %    211/206   185/202   191/207   194/196                        break, MD/TD                                                                   Shrink @90° C., MD/TD                                                                %    20/36     22/32     20/36     36/41                          Dynamic Puncture                                                                            cmkg/mil                                                                            3.24      2.62      3.07      2.59                           Haze         %    6.5       7.9       4.8       6.5                            Gloss        H.U. 70.7      73.2      79.8      76.9                           __________________________________________________________________________      .sup.(1) Dow 4001 type VLDPE (0.912 density)                                   .sup.(2) Dow XU 61509.32 type VLDPE (0.911 density, 0.5 MI)                    .sup.(3) Dow XU 61512.21 type VLDPE (0.901 density, 1.0 MI)              

The Table N results may be qualitatively compared with the Example 2 (Table J) results since both sets of film samples were prepared in small scale equipment, have the same type formulations with the same 0.912 density VLDPE-containing outer layer control sample, and are nonirradiated. More particularly, sample 8 (69.1% Tafmer A-0585, 22.5% EVA) has very high shrink (56/52%) and dynamic puncture strength (8.0 cmkg/mil) compared to 0.912 density VLDPE control sample 7. Low density VLDPE sample 27 also has substantially lower heat shrink (36/41%) than the present invention (at least 50% in at least one direction). Also, the dynamic puncture strength (2.59 cmkg/mil) is only about one third as high as the aforementioned invention sample 8.

EXAMPLE 7

In Example 7, three nonirradiated heat shrinkable film samples 28-30 were prepared by the previously described coextrusion-type double bubble process in a large scale (commercial type) system. The primary tube was about 2 inches inside diameter flat width, the final biaxially stretched tube flat width was about 10 inches inside and about 2 mils thick. Physical and optical properties of these films were measured and the results are summarized in Table O. The latter shows that sample 29 (0.901 density previously known VLDPE) provides higher shrink than sample 28 (0.912 density previously known VLDPE) or sample 30 (0.911 density previously known VLDPE). As previously explained this was probably due to greater flexibility of the lower density material.

The Table O results may be qualitatively compared with the Example 4 (Table L) results since both sets of three layer film samples were prepared in very similar large scale equipment, have the same type formulation with the same 0.912 density VLDPE-containing outer layer control sample, and are nonirradiated. More particularly, invention film embodiment sample 16 (40% Tafmer A-0585, 56% Exact 0633) has severalfold higher puncture strength than previously known 0.912 density VLDPE-containing sample 15. Accordingly, it is believed that a comparable embodiment of the inventive film would have substantially higher puncture strength than a 0.901 density previously known VLDPE-containing outer layer type film such as sample 30. From the shrink standpoint, invention sample 16 has very high values (57/60%) compared to sample 15, which is substantially the same composition as control sample 28 of this Example 7. Accordingly, a comparable embodiment of the inventive film would have substantially higher shrink values than the 32/39% values of sample 30.

Although preferred embodiments of this invention have been described in detail, it is contemplated that modifications thereof may be made and some preferred features may be employed without others, all within spirit and scope of the broad invention.

                                      TABLE O                                      __________________________________________________________________________     Low Density VLDPE Three Layer Films                                            Nonirradiated and Large Scale                                                                      Sample No.                                                               Units 28        29        30                                     __________________________________________________________________________     Formulation of                                                                               weight                                                                               70.6% VLDPE.sup.(1)                                                                      70.6% VLDPE.sup.(2)                                                                      70.6% VLDPE.sup.(3)                    Outer Layers        25.0% EVA 25.0% EVA 25.0% EVA                              Tensile Strength,                                                                            psi   13758/13633                                                                              12765/12298                                                                              14053/13595                            MD/TD                                                                          Elongation at %     197/221   209/242   184/207                                break, MD/TD                                                                   Shrink @90° C., MD/TD                                                                 %     34/39     42/44     32/39                                  Dynamic Puncture                                                                             cmkg/mil                                                                             2.79      2.94      3.18                                   Haze          %     5.7       5.2       6.4                                    Gloss         H.U.  79.4      79.5      76.5                                   __________________________________________________________________________      .sup.(1) Dow 4001 type VLDPE                                                   .sup.(2) Dow XU 61512.21 type VLDPE (0.901 density, 1.0 MI)                    .sup.(3) Dow XU 61509.32 type VLDPE (0.911 density, 0.5 MI)               

What is claimed is:
 1. A heat shrinkable, puncture resistant, biaxially stretched thermoplastic film suitable for use in fabricating bags for packaging food articles comprising a polyethylene which is a linear copolymer of ethylene and higher alpha olefin containing from 4 to 8 carbon atoms, having a density between about 0.88 and about 0.905 g/cm³, a melt index not exceeding about 1.0 g/10 min, a molecular weight/size distribution ratio Mw/Mn below about 3, a melting point below about 100° C., a Young's Modulus of below about 750 kg/cm², and wherein said film shrinks at least about 50 percent at a temperature of about 90° C. in at least one of the machine and transverse directions.
 2. A film according to claim 1 wherein said film is monolayer.
 3. A film according to claim 1 wherein said film is multilayer, and the ethylene alpha olefin copolymer comprises at least one layer of said film.
 4. A film according to claim 1 wherein said film is multilayer wherein one layer is an oxygen barrier material as a core with at least one other layer on each side thereof, and the ethylene alpha olefin copolymer comprises at least one of said other layers.
 5. A film according to claim 4 wherein the oxygen barrier-core layer is a copolymer of vinylidene chloride.
 6. A film according to claim 5 wherein the oxygen barrier-core layer is vinylidene chloride-vinyl chloride copolymer.
 7. A film according to claim 5 wherein the oxygen barrier-core layer is vinylidene chloride-methyl acrylate.
 8. A film according to claim 4 wherein the oxygen barrier-core layer is hydrolyzed ethylene vinyl acetate.
 9. A film according to claim 1 wherein the ethylene alpha olefin copolymer is blended with at least one other thermoplastic polymer.
 10. A film according to claim 9 wherein said other thermoplastic polymer is another ethylene alpha olefin copolymer.
 11. A film according to claim 10 wherein said another ethylene alpha olefin copolymer is prepared by a metallocene single site catalyst system.
 12. A film according to claim 9 wherein said other thermoplastic polymer is ethylene vinyl acetate.
 13. A film according to claim 9 wherein the ethylene alpha olefin copolymer is blended with another ethylene alpha olefin copolymer and ethylene vinyl acetate.
 14. A film according to claim 1 wherein said ethylene alpha olefin copolymer has a Vicat softening point not exceeding about 70° C.
 15. A film according to claim 1 wherein the ethylene alpha olefin copolymer is a butene copolymer having density of about 0.88 g/cm³, melt index of about 0.5 g/10 min; an Mw value of about 190,000, a Mn value of about 92,600, a melting point of about 67° C., a Young's Modulus of about 400 kg/cm², a dynamic puncture value of about 11.5 cmkg/mil, and a Vicat softening point of about 62° C.
 16. A film according to claim 1 which is crosslinked.
 17. A film according to claim 15 which is crosslinked by irradiation.
 18. A film according to claim 1 which shrinks at least about 55 percent in both the machine and traverse directions at 90° C.
 19. An irradiated film according to claim 15 comprising three layers including a vinylidene chloride-methyl acrylate copolymer oxygen barrier-core layer and an outer layer on each side of said barrier-core layer comprising a blend of between about 65 and 75% of said ethylene alpha olefin copolymer and between about 20 and 30% ethylene vinyl acetate, and said film shrinks at least about 55 percent in both the machine and transverse directions at 90° C.
 20. A film according to claim 1 wherein ethylene alpha olefin copolymer has a weight average molecular weight Mw of at least about 180,000 g/mole.
 21. A film according to claim 1 wherein the ethylene alpha olefin copolymer has a number average molecular weight of at least about 83,000 g/mole.
 22. A film according to claim 2 having dynamic puncture strength of at least about 10 cmkg/mil.
 23. A film according to claim 19 having dynamic puncture strength of at least about 3 cmkg/mil. 